Control of cryopreservation procedures on blood vessels using fiber x-ray diffraction

Primer Autor	Campos, H. Perez
Co-autores	Saldias, M. C. Silva, W. Machin, D. Suescun, L. Faccio, R. Mombru, A. W. Alvarez, I.
Título	Control of cryopreservation procedures on blood vessels using fiber x-ray diffraction
Editorial	ELSEVIER SCIENCE INC
Revista	TRANSPLANTATION PROCEEDINGS
Lenguaje	en
Resumen	Objetivo. Buscamos determinar variaciones en la organización de fibras a nivel molecular utilizando análisis de difracción de rayos X en muestras de vasos sanguíneos humanos después de procesos de criopreservación. Materiales y métodos. Se realizaron perfiles difractométricos en muestras de vasos aórticos y carotídeos criopreservados y descongelados (CVS) en comparación con las mismas muestras de vasos frescos (FVS). La difracción de rayos X se realizó en tejidos vasculares de 17 donantes cadavéricos después de su consentimiento informado. Las mediciones utilizaron un difractómetro de polvo Seifert Scintag PAD-II con radiación CuKα; lambda = 1,5418 angstrom. Los escaneos se evaluaron en el rango de 5 grados a 60 grados en modo theta -2theta, en el rango de 5 grados a 60 grados en 2-theta, con pasos de 0,1 grados y 10 segundos por paso. Se analizaron diez perfiles difractométricos aórticos y ocho carotídeos, utilizando superficies planimétricas diferenciales medidas bajo la curva de difracción de rayos X. Se analizaron perfiles difractográficos según intervalos basados en las edades de los donantes. Se obtuvo un coeficiente de perfil de ordenamiento (OPC) como el cociente entre la superficie planimétrica diferencial (DPS) de la difracción de ordenamiento vascular FVS versus CVS. Resultados. Hubo un perfil de ordenamiento disminuido según la edad: los donantes mayores mostraron menos ordenamiento que los más jóvenes. Siempre se confirmaron picos claros en d-espaciado de 2,86 angstrom y 2,15 angstrom (2-theta = 31,3 grados y 42,0 grados, respectivamente) a pesar de los diferentes perfiles de las muestras. El OPC mostró un perfil de ordenamiento más alto entre los CVS que FVS: 70% aortas y 62,5% carótidas. Conclusión. El procedimiento de criopreservación-descongelación no daña la organización fibrilar de los vasos.#Aim. We sought to determine variations in fiber organization at the molecular level using x-ray diffraction analyses on human blood vessel specimens after cryopreservation processes. Materials and Methods. Diffractometric profiles were performed on aortic and carotid cryopreserved-thawed vessel samples (CVS) versus the same fresh vessel samples (FVS). X-ray diffraction was performed on vascular tissues from 17 cadaveric donors after informed consent. Measurements utilized a Seifert Scintag PAD-II powder diffractometer with CuKa radiation; lambda = 1.5418 angstrom. Scans were evaluated in the 5 degrees to 60 degrees range in theta -2theta mode, in the 5 degrees to 60 degrees range in 2-theta, with steps 0.1 degrees and 10 seconds per step. Ten aortic and 8 carotid diffractometric profiles were analyzed, using differential planimetric surfaces measured under x-ray diffraction curve. Diffractographic profiles were analyzed according to intervals based upon the ages of the donors. An ordering profile coefficient (OPC) was obtained as the quotient between the differential planimetric surface (DPS) of FVS versus CVS vessel ordering diffraction. Results. There was a decreased ordering profile according to age : older donors showed less ordering than younger ones. Clear peaks at d-spacing of 2.86 angstrom and 2.15 angstrom (2-theta = 31.3 degrees and 42.0 degrees, respectively) were always confirmed despite the different profiles of samples. OPC showed a higher ordering profile among the CVS than FVS: 70% aortas and 62.5% carotids. Conclusion. The cryopreserved-thawed procedure does not damage the fibrillar organization of vessels.
Tipo de Recurso	Artículo de conferencia
doi	10.1016/j.transproceed.2008.02.025
Formato Recurso	pdf
Palabras Claves	HUMAN ARTERIES MECHANICAL-PROPERTIES EXTRACELLULAR-MATRIX IN-VIVO FRESH HOMOGRAFTS VITRIFICATION PRESERVATION PROSTHESES TISSUES ARTERIAS HUMANAS PROPIEDADES MECÁNICAS MATRIZ EXTRACELULAR IN VIVO FRESCO HOMOINJERTOS VITRIFICACIÓN CONSERVACIÓN PRÓTESIS TEJIDOS
Ubicación del archivo	http://dx.doi.org/10.1016/j.transproceed.2008.02.025
Materias	HUMAN ARTERIES MECHANICAL-PROPERTIES EXTRACELLULAR-MATRIX IN-VIVO FRESH HOMOGRAFTS VITRIFICATION PRESERVATION PROSTHESES TISSUES ARTERIAS HUMANAS PROPIEDADES MECÁNICAS MATRIZ EXTRACELULAR IN VIVO FRESCO HOMOINJERTOS VITRIFICACIÓN CONSERVACIÓN PRÓTESIS TEJIDOS
Título de la cita (Recomendado-único)	Control of cryopreservation procedures on blood vessels using fiber x-ray diffraction
Revista/Libro	TRANSPLANTATION PROCEEDINGS
Tipo de ruta	suscripción
Access Rights	restringido
Derechos de acceso	restringido
Identificador alternativo	PMID 18454983
Idioma	en
Identificador del recurso (Mandatado-único)	Artículo de conferencia
Versión del recurso (Recomendado-único)	versión publicada
Lugar de la conferencia(Recomendado-repetible)	Joint Congress of the 10th Transplantation-Society-of-Brazil/19th Latin-American-and-Caribbean-Transplantation-Society/6th Luso-Brazilian-Transplantation-Society
Fecha de la conferencia(Recomendado-repetible)	SEP 02-05, 2007 SEP 02-05, 2007
Editorial	ELSEVIER SCIENCE INC
ISSN	0041-1345
Página de inicio (Recomendado-único)	668
Página final (Recomendado-único)	674
Categoría WOS	Inmunología Cirugía Trasplante Immunology Surgery Transplantation
Formato	pdf
Id de Web of Science	WOS:000255527600006